Flux growth and optical properties of K7CaY2(B5O10)3 nonlinear crystal /A. B. Kuznetsov, D. M. Ezhov, K. A. Kokh [et al.]

Электронный ресурс
Другой Автор
Ezhov, Dmitry M.
Kokh, Konstantin A.
Kononova, N. G.
Shevchenko, V. S.
Rashchenko, S. V.
Pestryakov, E. V
Svetlichnyi, Valerii A.
Lapin, Ivan N.
Kokh, A. E.
Kuznetsov, Artem B.
Источник
Materials research bulletin 2018 Vol. 107. P. 333-338
Аннотация
Non-centrosymmetric borates K7CaY2(B5O10)3 have been synthesized by solid state reaction and the crystals were successfully grown by the top seeded solution growth method using K2O-B2O3-CaF2 flux. According to the single X-ray diffraction, the structure belongs to the R32 space group with lattice parameters a = 13.2516(2) Å and c = 14.9679(3) Å. IR, Raman, absorption spectra as well as data on melting temperature were obtained for the crystal. The short edge of UV absorption and SHG intensity comparable with KH2PO4 (KDP) suggests that this crystal is a promising nonlinear-optical material.
Всего оценка: 0
Нет записей для отображения.
 
 
 
02190nab a2200421 c 4500
001
 
 
vtls000788535
003
 
 
RU-ToGU
005
 
 
20201123175200.0
007
 
 
cr |
008
 
 
201118|2018    enk     s         a eng dd
024
7
$a 10.1016/j.materresbull.2018.07.037 $2 doi
035
$a to000788535
039
9
$a 202011231752 $b cat34 $c 202011181602 $d VLOAD $y 202011181556 $z VLOAD
040
$a RU-ToGU $b rus $c RU-ToGU
245
1
0
$a Flux growth and optical properties of K7CaY2(B5O10)3 nonlinear crystal $c A. B. Kuznetsov, D. M. Ezhov, K. A. Kokh [et al.]
336
$a Текст
337
$a электронный
520
3
$a Non-centrosymmetric borates K7CaY2(B5O10)3 have been synthesized by solid state reaction and the crystals were successfully grown by the top seeded solution growth method using K2O-B2O3-CaF2 flux. According to the single X-ray diffraction, the structure belongs to the R32 space group with lattice parameters a = 13.2516(2) Å and c = 14.9679(3) Å. IR, Raman, absorption spectra as well as data on melting temperature were obtained for the crystal. The short edge of UV absorption and SHG intensity comparable with KH2PO4 (KDP) suggests that this crystal is a promising nonlinear-optical material.
653
$a оптические свойства
653
$a нелинейные кристаллы
653
$a нецентросимметричные бораты
655
4
$a статьи в журналах
700
1
$a Ezhov, Dmitry M.
700
1
$a Kokh, Konstantin A.
700
1
$a Kononova, N. G.
700
1
$a Shevchenko, V. S.
700
1
$a Rashchenko, S. V.
700
1
$a Pestryakov, E. V
700
1
$a Svetlichnyi, Valerii A.
700
1
$a Lapin, Ivan N.
700
1
$a Kokh, A. E.
700
1
$a Kuznetsov, Artem B.
773
0
$t Materials research bulletin $d 2018 $g Vol. 107. P. 333-338 $x 0025-5408
852
4
$a RU-ToGU
856
4
$u http://vital.lib.tsu.ru/vital/access/manager/Repository/vtls:000788535
908
$a статья
999
$a VIRTUA               
999
$a VTLSSORT0070*0080*0240*0350*0400*2450*3360*3370*5200*6530*6531*6532*6550*7009*7000*7001*7002*7003*7004*7005*7006*7007*7008*7730*8520*8560*9080*9992
Нет комментариев.
Предмет
статьи в журналах
Резюме
Non-centrosymmetric borates K7CaY2(B5O10)3 have been synthesized by solid state reaction and the crystals were successfully grown by the top seeded solution growth method using K2O-B2O3-CaF2 flux. According to the single X-ray diffraction, the structure belongs to the R32 space group with lattice parameters a = 13.2516(2) Å and c = 14.9679(3) Å. IR, Raman, absorption spectra as well as data on melting temperature were obtained for the crystal. The short edge of UV absorption and SHG intensity comparable with KH2PO4 (KDP) suggests that this crystal is a promising nonlinear-optical material.