Optical properties of β-BBO and potential for THz applications /N. A. Nikolaev, Yu. M. Andreev, V. D. Antsygin [et al.]

Электронный ресурс
Другой Автор
Andreev, Yury M. 1946-
Antsygin, Valery D.
Bekker, T. B.
Ezhov, Dmitry M.
Kokh, A. E.
Kokh, Konstantin A.
Lanskii, Grigory V.
Mamrashev, Alexander A.
Svetlichnyi, Valerii A.
Nikolaev, Nazar A.
Источник
Journal of Physics: Conference Series 2018 Vol. 951. P. 012003 (1-4)
Аннотация
The anisotropy of optical properties of high quality beta barium borate crystal (β-BaB2O4, β-BBO) was studied in the main transparency window by using classic spectroscopic methods and in the range of 0.2 – 2 THz by using THz time-domain spectroscopy. β-BBO crystals were grown by the top-seeded solution technique in a highly resistive furnace with a heat field of 3-fold axis symmetry. At room temperature (RT), absorption coefficient in the maximal transparency window in grown crystals did not exceed 0.05 cm-1. Strong absorption anisotropy was observed in 3 – 5 μm and the THz range. At 1 THz absorption coefficients for e and o wave were, respectively, 7 cm-1 and 21 cm-1 at RT; 2 cm-1 and 10 cm-1 at 81 K. At the most attractive for out-of-door applications range < 0.4 THz the absorption coefficient is found to be very low: below 0.2 cm-1 at RT and 1 cm-1 at 81 K. Refractive indices dispersions measured by THz-TDS were approximated in the form of Sellmeier equations. Birefringence is found quite large for phase matched difference frequency generation (DFG) or down-conversion into the THz range (THz-DFG) under near IR pump at RT and 81 K. Type II (oe-o and eo-o), and type I (ee-e) three wave interactions can be realized at RT. THz-DFG of Nd:YAG laser and KTP OPO can be realized by type II (oe-o) three-wave interaction. For selected spectral ranges of femtosecond Ti:Sapphire laser efficient phase matched and group velocity matched optical rectification can be realized by another two types of three wave interactions. Accounting other well-known attractive physical properties of β-BBO crystal, wide application in THz technique can be forecasted.
Всего оценка: 0
Нет записей для отображения.
 
 
 
03316nab a2200433 c 4500
001
 
 
vtls000788534
003
 
 
RU-ToGU
005
 
 
20201123175500.0
007
 
 
cr |
008
 
 
201118|2018    enk     s         a eng d
024
7
$a 10.1088/1742-6596/951/1/012003 $2 doi
035
$a to000788534
039
9
$a 202011231755 $b cat34 $c 202011181602 $d VLOAD $y 202011181555 $z VLOAD
040
$a RU-ToGU $b rus $c RU-ToGU
245
1
0
$a Optical properties of β-BBO and potential for THz applications $c N. A. Nikolaev, Yu. M. Andreev, V. D. Antsygin [et al.]
336
$a Текст
337
$a электронный
504
$a Библиогр.: 5 назв.
520
3
$a The anisotropy of optical properties of high quality beta barium borate crystal (β-BaB2O4, β-BBO) was studied in the main transparency window by using classic spectroscopic methods and in the range of 0.2 – 2 THz by using THz time-domain spectroscopy. β-BBO crystals were grown by the top-seeded solution technique in a highly resistive furnace with a heat field of 3-fold axis symmetry. At room temperature (RT), absorption coefficient in the maximal transparency window in grown crystals did not exceed 0.05 cm-1. Strong absorption anisotropy was observed in 3 – 5 μm and the THz range. At 1 THz absorption coefficients for e and o wave were, respectively, 7 cm-1 and 21 cm-1 at RT; 2 cm-1 and 10 cm-1 at 81 K. At the most attractive for out-of-door applications range < 0.4 THz the absorption coefficient is found to be very low: below 0.2 cm-1 at RT and 1 cm-1 at 81 K. Refractive indices dispersions measured by THz-TDS were approximated in the form of Sellmeier equations. Birefringence is found quite large for phase matched difference frequency generation (DFG) or down-conversion into the THz range (THz-DFG) under near IR pump at RT and 81 K. Type II (oe-o and eo-o), and type I (ee-e) three wave interactions can be realized at RT. THz-DFG of Nd:YAG laser and KTP OPO can be realized by type II (oe-o) three-wave interaction. For selected spectral ranges of femtosecond Ti:Sapphire laser efficient phase matched and group velocity matched optical rectification can be realized by another two types of three wave interactions. Accounting other well-known attractive physical properties of β-BBO crystal, wide application in THz technique can be forecasted.
653
$a оптические свойства
653
$a терагерцовый диапазон
653
$a бета-борат бария
655
4
$a статьи в журналах
700
1
$a Andreev, Yury M. $d 1946-
700
1
$a Antsygin, Valery D.
700
1
$a Bekker, T. B.
700
1
$a Ezhov, Dmitry M.
700
1
$a Kokh, A. E.
700
1
$a Kokh, Konstantin A.
700
1
$a Lanskii, Grigory V.
700
1
$a Mamrashev, Alexander A.
700
1
$a Svetlichnyi, Valerii A.
700
1
$a Nikolaev, Nazar A.
773
0
$t Journal of Physics: Conference Series $d 2018 $g Vol. 951. P. 012003 (1-4) $x 1742-6588
852
4
$a RU-ToGU
856
4
$u http://vital.lib.tsu.ru/vital/access/manager/Repository/vtls:000788534
908
$a статья
999
$a VIRTUA               
999
$a VTLSSORT0070*0080*0240*0350*0400*2450*3360*3370*5040*5200*6530*6531*6532*6550*7009*7000*7001*7002*7003*7004*7005*7006*7007*7008*7730*8520*8560*9080*9992
Нет комментариев.
Предмет
статьи в журналах
Резюме
The anisotropy of optical properties of high quality beta barium borate crystal (β-BaB2O4, β-BBO) was studied in the main transparency window by using classic spectroscopic methods and in the range of 0.2 – 2 THz by using THz time-domain spectroscopy. β-BBO crystals were grown by the top-seeded solution technique in a highly resistive furnace with a heat field of 3-fold axis symmetry. At room temperature (RT), absorption coefficient in the maximal transparency window in grown crystals did not exceed 0.05 cm-1. Strong absorption anisotropy was observed in 3 – 5 μm and the THz range. At 1 THz absorption coefficients for e and o wave were, respectively, 7 cm-1 and 21 cm-1 at RT; 2 cm-1 and 10 cm-1 at 81 K. At the most attractive for out-of-door applications range < 0.4 THz the absorption coefficient is found to be very low: below 0.2 cm-1 at RT and 1 cm-1 at 81 K. Refractive indices dispersions measured by THz-TDS were approximated in the form of Sellmeier equations. Birefringence is found quite large for phase matched difference frequency generation (DFG) or down-conversion into the THz range (THz-DFG) under near IR pump at RT and 81 K. Type II (oe-o and eo-o), and type I (ee-e) three wave interactions can be realized at RT. THz-DFG of Nd:YAG laser and KTP OPO can be realized by type II (oe-o) three-wave interaction. For selected spectral ranges of femtosecond Ti:Sapphire laser efficient phase matched and group velocity matched optical rectification can be realized by another two types of three wave interactions. Accounting other well-known attractive physical properties of β-BBO crystal, wide application in THz technique can be forecasted.