Influence of wood flour additive on porous structure and strength properties of moulded alumina /T. Bugrova, A. Tatarkina, I. Zhukov, G. Mamontov

Электронный ресурс
Другой Автор
Bugrova, Tatiana A.
Mamontov, Grigory V.
Zhukov, Ilya A.
Tatarkina, Anastasia
Источник
Key engineering materials 2015 Vol. 670. P. 139-143
Аннотация
The moulded Al2O3 materials prepared by mixing of thermochemically activated aluminum trihydroxide (TCA ATH) with wood flour were proposed to be used as promising porous catalyst support for various processes. A series of Al2O3 supports with different wood flour loading (0, 2 and 5 %wt.) were studied by SEM, low-temperature N2 sorption, XRD, granule strength and water-absorbing capacity. It was shown that supports were characterized by porous structure with mesopore sizes of 2-20 nm and specific surface area of 159-186 m2/g. The increase of the amount of wood flour leads to increase of the share of pore volume with wider than 10 nm and the decrease of the strength of alumina granules. Thus, optimization of preparation conditions allows obtaining alumina materials with desired porous structure.
Всего оценка: 0
Нет записей для отображения.
 
 
 
02165nab a2200337 c 4500
001
 
 
vtls000569822
003
 
 
RU-ToGU
005
 
 
20170418085700.0
007
 
 
cr |
008
 
 
170417|2015    sz      s         a eng dd
024
7
$a 10.4028/www.scientific.net/KEM.670.139 $2 doi
035
$a to000569822
039
9
$a 201704180857 $b cat202 $c 201704171512 $d VLOAD $y 201704171311 $z VLOAD
040
$a RU-ToGU $b rus $c RU-ToGU
245
1
0
$a Influence of wood flour additive on porous structure and strength properties of moulded alumina $c T. Bugrova, A. Tatarkina, I. Zhukov, G. Mamontov
504
$a Библиогр.: 15 назв.
520
3
$a The moulded Al2O3 materials prepared by mixing of thermochemically activated aluminum trihydroxide (TCA ATH) with wood flour were proposed to be used as promising porous catalyst support for various processes. A series of Al2O3 supports with different wood flour loading (0, 2 and 5 %wt.) were studied by SEM, low-temperature N2 sorption, XRD, granule strength and water-absorbing capacity. It was shown that supports were characterized by porous structure with mesopore sizes of 2-20 nm and specific surface area of 159-186 m2/g. The increase of the amount of wood flour leads to increase of the share of pore volume with wider than 10 nm and the decrease of the strength of alumina granules. Thus, optimization of preparation conditions allows obtaining alumina materials with desired porous structure.
653
$a формование
653
$a пористая структура
653
$a прочностные свойства гранул
655
4
$a статьи в журналах
700
1
$a Bugrova, Tatiana A.
700
1
$a Mamontov, Grigory V.
700
1
$a Zhukov, Ilya A.
700
1
$a Tatarkina, Anastasia
773
0
$t Key engineering materials $d 2015 $g Vol. 670. P. 139-143 $x 1013-9826
852
4
$a RU-ToGU
856
7
$u http://vital.lib.tsu.ru/vital/access/manager/Repository/vtls:000569822
908
$a статья
999
$a VIRTUA               
999
$a VTLSSORT0010*0030*0050*0070*0080*0240*0350*0390*0400*2450*5040*5200*6530*6531*6532*6550*7000*7003*7002*7001*7730*8520*8560*9080*9992
Нет комментариев.
Предмет
статьи в журналах
Резюме
The moulded Al2O3 materials prepared by mixing of thermochemically activated aluminum trihydroxide (TCA ATH) with wood flour were proposed to be used as promising porous catalyst support for various processes. A series of Al2O3 supports with different wood flour loading (0, 2 and 5 %wt.) were studied by SEM, low-temperature N2 sorption, XRD, granule strength and water-absorbing capacity. It was shown that supports were characterized by porous structure with mesopore sizes of 2-20 nm and specific surface area of 159-186 m2/g. The increase of the amount of wood flour leads to increase of the share of pore volume with wider than 10 nm and the decrease of the strength of alumina granules. Thus, optimization of preparation conditions allows obtaining alumina materials with desired porous structure.